Correlation Between Ball Milling Parameters and Microstructure Parameters of Nanocopper Using XRD Method
O. Boytsov4, F. Bernard1, E. Gaffet2, Y. Champion3 and A. Ustinov4 1LRRS UMR 5613 CNRS/Université de Bourgogne - BP 47870 21078 Dijon (France), E-mail: fbernard@u-bourgogne.fr 2Nanomaterials Research Group UMR 5060 CNRS/UTBM - 90010 Belfort (France), E-mail: eric.gaffet@utbm.fr 3CECM - CNRS, 15 rue Georges Urbain, 94407 Vitry-sur-Seine (France), E-mail: yannick.champion@glvt-cnrs.fr 4Institute for Metal Physics, Pr. Vernadskogo, 36, Kiev 03142 (Ukraine), E-mail: ustinov@paton-icebt.kiev.ua
Страницы: 131-136
Аннотация
The microstructure evolution of Cu-nanostructured powders versus the ball milling conditions was investigated using X-ray diffraction analysis. The characteristics of as-milled Cu powder microstructure in terms of crystallite size, dislocations and twin boundary densities were determined by fitting the simulated X-ray diffraction peak profiles to the experimental ones in order to establish a correlation between the powder microstructure and the ball milling parameters. It was shown that the simulated X-ray diffraction peak profiles agree satisfactorily with the experimental ones taking into account transmission electronic microscopy observations where twin boundaries and dislocations were observed.
Наш сайт использует куки. Продолжая им пользоваться, вы соглашаетесь на обработку персональных данных в соответствии с политикой конфиденциальности. Подробнее