Издательство СО РАН

Издательство СО РАН

Адрес Издательства СО РАН: Россия, 630090, а/я 187
Новосибирск, Морской пр., 2

soran2.gif

Baner_Nauka_Sibiri.jpg


Яндекс.Метрика

Array
(
    [SESS_AUTH] => Array
        (
            [POLICY] => Array
                (
                    [SESSION_TIMEOUT] => 24
                    [SESSION_IP_MASK] => 0.0.0.0
                    [MAX_STORE_NUM] => 10
                    [STORE_IP_MASK] => 0.0.0.0
                    [STORE_TIMEOUT] => 525600
                    [CHECKWORD_TIMEOUT] => 525600
                    [PASSWORD_LENGTH] => 6
                    [PASSWORD_UPPERCASE] => N
                    [PASSWORD_LOWERCASE] => N
                    [PASSWORD_DIGITS] => N
                    [PASSWORD_PUNCTUATION] => N
                    [LOGIN_ATTEMPTS] => 0
                    [PASSWORD_REQUIREMENTS] => Пароль должен быть не менее 6 символов длиной.
                )

        )

    [SESS_IP] => 3.236.13.53
    [SESS_TIME] => 1632074119
    [BX_SESSION_SIGN] => 9b3eeb12a31176bf2731c6c072271eb6
    [fixed_session_id] => db8a24a37eef4fd06433820b65b33fac
    [SALE_USER_ID] => 0
    [UNIQUE_KEY] => 23f2bd95165ae98089579827e91c1abe
    [BX_LOGIN_NEED_CAPTCHA_LOGIN] => Array
        (
            [LOGIN] => 
            [POLICY_ATTEMPTS] => 0
        )

)

Поиск по журналу

Химия в интересах устойчивого развития

2007 год, номер 2

Mechanochemical Synthesis of Proton Conductive M3H(SO4)2 (M = Na, K, Rb) Crystals

T. Tezuka, Y. Yamashita, A. Hayashi, K. Tadanaga and M. Tatsumisago
Department of Applied Chemistry, Graduate School of Engineering,
Osaka Prefecture University, Sakai, Osaka 599-8531 (Japan)
E-mail: t-tezuka@chem.osakafu-u.ac.jp
Страницы: 237-241

Аннотация

M3H(SO4)2 (M = Na, K, Rb) crystals, which are known to undergo superprotonic phase transition in the case of M = K and Rb, were prepared via mechanochemical process from equimolar M2SO4 and MHSO4. The phase transitions of M3H(SO4)2 prepared by mechanical milling using a high energy ball mill apparatus were confirmed from DTA-TG and conductivity measurements, although the phase transition temperatures were slightly lower than that of M3H(SO4)2 prepared via solution process. The Rb3H(SO4)2 prepared by mechanical milling showed reproducible ionic conductivity of 1×10-3 S/cm at 230 oC under dry N2 atmosphere.