Density and thermal expansion of LiK3Pb4 liquid alloy .
A.Sh. Agazhanov, R.A. Khairulin, R.N. Abdullaev, S.V. Stankus
Kutateladze Institute of Thermophysics SB RAS, Novosibirsk, Russia
Keywords: density, thermal expansion, lithium-potassium-lead alloy, melt, gamma-ray attenuation technique
Abstract
A density and a volumetric thermal expansion coefficient of the LiK3Pb4 ternary alloy (12.5 at. % Li; 37.5 at. % K; 50.0 at. % Pb) in the liquid state are measured for the first time. Thermal properties are studied using a gamma-ray attenuation technique in the range from the liquidus temperature TL = 812 K to 990 K. The LiK3Pb4 solid alloy is known to be an intermetallic compound. Its thermal analysis at cooling from the liquid state carried out in this work has shown that the compound is likely formed by a peritectic reaction at 789 K. Based on the experimental results obtained, a table of recommended values for the volumetric properties of the LiK3Pb4 melt has been developed in the studied temperature range.
|