Издательство СО РАН

Издательство СО РАН

Адрес Издательства СО РАН: Россия, 630090, а/я 187
Новосибирск, Морской пр., 2

soran2.gif

Baner_Nauka_Sibiri.jpg


Яндекс.Метрика

Array
(
    [SESS_AUTH] => Array
        (
            [POLICY] => Array
                (
                    [SESSION_TIMEOUT] => 24
                    [SESSION_IP_MASK] => 0.0.0.0
                    [MAX_STORE_NUM] => 10
                    [STORE_IP_MASK] => 0.0.0.0
                    [STORE_TIMEOUT] => 525600
                    [CHECKWORD_TIMEOUT] => 525600
                    [PASSWORD_LENGTH] => 6
                    [PASSWORD_UPPERCASE] => N
                    [PASSWORD_LOWERCASE] => N
                    [PASSWORD_DIGITS] => N
                    [PASSWORD_PUNCTUATION] => N
                    [LOGIN_ATTEMPTS] => 0
                    [PASSWORD_REQUIREMENTS] => Пароль должен быть не менее 6 символов длиной.
                )

        )

    [SESS_IP] => 3.87.209.162
    [SESS_TIME] => 1711662708
    [BX_SESSION_SIGN] => 9b3eeb12a31176bf2731c6c072271eb6
    [fixed_session_id] => 617c55c4233f47616b19789c15922b96
    [UNIQUE_KEY] => 873a32af15a4fb64dac411cfa4a359a7
    [BX_LOGIN_NEED_CAPTCHA_LOGIN] => Array
        (
            [LOGIN] => 
            [POLICY_ATTEMPTS] => 0
        )

)

Поиск по журналу

Журнал структурной химии

2011 год, номер 2

PHASE FORMATION IN MIXED TiO2-ZrO2 OXIDES PREPARED BY SOL-GEL METHOD

E. Kraleva1, M.L. Saladino2, R. Matassa3, E. Caponetti4, S. Enzo5, A. Spojakina1
1 Institute of Catalysis Bulgarian Academy of Sciences
2 Dipartimento di Chimica ″S. Cannizzaro″ Università di Palermo and INSTM-Udr Palermo
3 Centro Grandi Apparecchiature-UniNetLab, Università di Palermo
4 Dipartimento di Chimica ″S. Cannizzaro″ Università di Palermo and INSTM-Udr Palermo Centro Grandi Apparecchiature-UniNetLab, Università di Palermo
5 Dipartimento di Chimica, Università di Sassari and INSTM-Udr Sassari
e_kraleva@yahoo.com
Ключевые слова: TiO2-ZrO2 mixed oxides, sol-gel method, srilankite, Rietveld method
Страницы: 340-348

Аннотация

Pure titania, zirconia, and mixed oxides (3-37 mol.% of ZrO2) are prepared using the sol-gel method and calcined at different temperatures. The calcined samples are characterized by Raman spectroscopy, X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy, and nitrogen adsorption porosimetry. Measurements reveal a thermal stability of the titania anatase phase that slightly increases in the presence of 3-13 mol.% of zirconia. Practically, the titania anatase-rutile phase transformation is hindered during the temperature increase above 700 °C. The mixed oxide with 37 mol.% of ZrO2 treated at 550 °C shows a new single amorphous phase with a surface area of the nanoparticles double with respect to the other crystalline samples and the formed srilankite structure (at 700 °C). The anatase phase is not observed in the sample containing 37 mol.% of ZrO2. The treatment at 700 °C causes the formation of the srilankite (Ti0.63Zr0.37Ox) phase.