Издательство СО РАН

Издательство СО РАН

Адрес Издательства СО РАН: Россия, 630090, а/я 187
Новосибирск, Морской пр., 2

soran2.gif

Baner_Nauka_Sibiri.jpg


Яндекс.Метрика

Array
(
    [SESS_AUTH] => Array
        (
            [POLICY] => Array
                (
                    [SESSION_TIMEOUT] => 24
                    [SESSION_IP_MASK] => 0.0.0.0
                    [MAX_STORE_NUM] => 10
                    [STORE_IP_MASK] => 0.0.0.0
                    [STORE_TIMEOUT] => 525600
                    [CHECKWORD_TIMEOUT] => 525600
                    [PASSWORD_LENGTH] => 6
                    [PASSWORD_UPPERCASE] => N
                    [PASSWORD_LOWERCASE] => N
                    [PASSWORD_DIGITS] => N
                    [PASSWORD_PUNCTUATION] => N
                    [LOGIN_ATTEMPTS] => 0
                    [PASSWORD_REQUIREMENTS] => Пароль должен быть не менее 6 символов длиной.
                )

        )

    [SESS_IP] => 3.144.244.44
    [SESS_TIME] => 1713403661
    [BX_SESSION_SIGN] => 9b3eeb12a31176bf2731c6c072271eb6
    [fixed_session_id] => c52bf1ac73905a341d2016dbf311b973
    [UNIQUE_KEY] => 98d1632a1a0d9685fdafb9035abb7b67
    [BX_LOGIN_NEED_CAPTCHA_LOGIN] => Array
        (
            [LOGIN] => 
            [POLICY_ATTEMPTS] => 0
        )

)

Поиск по журналу

Химия в интересах устойчивого развития

2003 год, номер 1

XPS Study of Metal-Support Interaction in Ru/MgO Catalyst for Low-Temperature Ammonia Synthesis

Yu. V. LARICHEV1, 2, B. L. MOROZ2, I. P. PROSVIRIN2, V. A. LIKHOLOBOV1, 2 and V. I. BUKHTIYAROV2
1Novosibirsk State University,
Ul. Pirogova 2, Novosibirsk 630090 (Russia), E-mail: prsv@catalysis.nsk.su
2 G. K. Boreskov Institute of Catalysis, Siberian Branch of the Russian Academy of Sciences,
Pr. Akademika Lavrentyeva 5, Novosibirsk 630090 (Russia), E-mail: moroz@catalysis.nsk.su
Страницы: 155-160

Аннотация

The catalytic system Ru/MgO has been characterized by TEM and XPS in the Ru 3d, Cl 2p and O1s regions. It was shown, that the treatment of the sample with H2 at 450 °Ñ leads to reduction of supported Ru (III, IV) chloride complexes to Ru metal crystallites of 2–5 nm in size (the surface atomic ratio Ru : Cl of reduced sample is 6.2). The shift of Ru 3d peak (279.5 eV) to lower bond energy (BE) found for Ru/MgO sample as compared with bulk Ru metal (280.2 eV) is proved to be due to the differential charging effect. The value of this effect was estimated by a comparison of the valence band spectrum of supported Ru particles with that of bulk Ru. Taking the differential charging into account, the "true" value BE of Ru 3d5/2 (280.5 eV) was determined. The shift of Ru 3d peak towards the higher BE values may indicate the electron-withdrawing effect of MgO surface to supported Ru particles.